The objective of this project was to examine the effects of bulk water chemistry on concrete corrosion and autogenous repair of concrete. This project identified that autogenous healing can be controlled by water chemistry, and it can be an effective method of sealing small cracks that initiate in concrete before they develop into larger cracks that can cause failure. When high levels of magnesium and silicon are present this seal can develop high strength. Carbonation of internal surfaces was not detected when cracks were sealed via autogenous healing. In some cases, water permeability and chloride diffusion are impeded by autogenous healing regardless of strength attained.

The objective of this project was to examine the effects of bulk water chemistry on concrete corrosion and autogenous repair of concrete. This project identified that autogenous healing can be controlled by water chemistry, and it can be an effective method of sealing small cracks that initiate in concrete before they develop into larger cracks that can cause failure. When high levels of magnesium and silicon are present this seal can develop high strength. Carbonation of internal surfaces was not detected when cracks were sealed via autogenous healing. In some cases, water permeability and chloride diffusion are impeded by autogenous healing regardless of strength attained.

The objective of this project was to examine the effects of bulk water chemistry on concrete corrosion and autogenous repair of concrete. This project identified that autogenous healing can be controlled by water chemistry, and it can be an effective method of sealing small cracks that initiate in concrete before they develop into larger cracks that can cause failure. When high levels of magnesium and silicon are present this seal can develop high strength. Carbonation of internal surfaces was not detected when cracks were sealed via autogenous healing. In some cases, water permeability and chloride diffusion are impeded by autogenous healing regardless of strength attained.